Convergence problem in RF module

Posted 1 apr 2013, 07:16 GMT-4 Materials, Studies & Solvers Version 5.1 3 Replies

Debadrita Paria
Send Private Message Flag post as spam

Please login with a confirmed email address before reporting spam

I am doing some plasmonics simulation using silver nano particles in comsol. For silver particle convergence is either very very slow or there is no convergence in most cases for some specific wavelengths. The same model works fine for gold nano particles. Kindly help.
3 Replies Last Post 20 gen 2017, 11:44 GMT-5
COMSOL Moderator

Hello Debadrita Paria

Your Discussion has gone 30 days without a reply. If you still need help with COMSOL and have an on-subscription license, please visit our Support Center for help.

If you do not hold an on-subscription license, you may find an answer in another Discussion or in the Knowledge Base.

Shuai Hou
Send Private Message Flag post as spam

Please login with a confirmed email address before reporting spam

Posted: 1 decade ago 23 set 2014, 23:11 GMT-4
Please try the direct solver instead of the iterative solver. I had exactly the same problem (extremely slow convergence at about 360 nm for a silver nanocrystal), and the direct solver worked perfectly.
Please try the direct solver instead of the iterative solver. I had exactly the same problem (extremely slow convergence at about 360 nm for a silver nanocrystal), and the direct solver worked perfectly.
Seojoo Lee
Send Private Message Flag post as spam

Please login with a confirmed email address before reporting spam

Posted: 8 years ago 20 gen 2017, 11:10 GMT-5
I was stuck in same problem.
Thanks for your comment. !
I was stuck in same problem. Thanks for your comment. !
Walter Frei COMSOL Employee

Please login with a confirmed email address before reporting spam

Posted: 8 years ago 20 gen 2017, 11:44 GMT-5
Hello All,

Having to use a direct solver is also often a sign that you've undermeshed the problem, especially in the silver material domains.
If you're dealing with a model that has lossy materials, please read:
www.comsol.com/blogs/modeling-of-materials-in-wave-electromagnetics-problems/
www.comsol.com/blogs/simulation-tools-for-solving-wave-electromagnetics-problems/

Meshing more finely may improve solution speed when using the iterative solver (and although a more finely meshed problem will use more memory, the iterative solver uses much less memory that the direct solver, so you generally come out ahead.)

Best Regards,
Hello All, Having to use a direct solver is also often a sign that you've undermeshed the problem, especially in the silver material domains. If you're dealing with a model that has lossy materials, please read: https://www.comsol.com/blogs/modeling-of-materials-in-wave-electromagnetics-problems/ https://www.comsol.com/blogs/simulation-tools-for-solving-wave-electromagnetics-problems/ Meshing more finely may improve solution speed when using the iterative solver (and although a more finely meshed problem will use more memory, the iterative solver uses much less memory that the direct solver, so you generally come out ahead.) Best Regards,