Hi all,

Do you have any idea of modeling (simulation) of laminates , e.g. bi-layer composites having layers with different elastic modulus avoiding the so called 'free edge effect' (a stress singularity at the free edge).

i am using Comsol 4.3b and having this problem while i try to work with modeling creep in bi-layers

thanks for your time
-Tesfaye
1 Reply Last Post 31 mar 2017, 03:18 GMT-4
COMSOL Moderator

Hello Tesfaye Tadesse Molla

Your Discussion has gone 30 days without a reply. If you still need help with COMSOL and have an on-subscription license, please visit our Support Center for help.

If you do not hold an on-subscription license, you may find an answer in another Discussion or in the Knowledge Base.

Tobias Krüger
Send Private Message Flag post as spam

Please login with a confirmed email address before reporting spam

Posted: 8 years ago 31 mar 2017, 03:18 GMT-4
Hello Tesfaye,

Could you find a proper way of getting around the singularity? I'm dealing with the same problem. I'd like to set up a model to investigate in the thermomechanical behaviour of CMC's, but none of my approaches led to convergence of the interlaminar stresses.

I was thinking about smoothening the properties with a step-function within a "thin elastic layer", but I think I'm missing information within this approach since we're dealing with anisotropic materials.

Any help would be highly appreciated.
Thank you,

Tobias Krüger

Hello Tesfaye, Could you find a proper way of getting around the singularity? I'm dealing with the same problem. I'd like to set up a model to investigate in the thermomechanical behaviour of CMC's, but none of my approaches led to convergence of the interlaminar stresses. I was thinking about smoothening the properties with a step-function within a "thin elastic layer", but I think I'm missing information within this approach since we're dealing with anisotropic materials. Any help would be highly appreciated. Thank you, Tobias Krüger